點(diǎn)擊圖片查看大圖| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 融體流動(dòng)速率 | 200℃/5kg | ASTM D-1238 | 1.0 | g/10min |
| 熔體流動(dòng)速率 | 200℃/5kg | ASTM D-1238 | 10 | g/10min | |
| 密度 | ASTM D-792 | 1.03 | |||
| 吸水率 | ASTM D-570 | 0.3 | WT% | ||
| 物理性能 | 成型收縮率 | ASTM D-955 | 0.4 | % | |
| 機(jī)械性能 | IZOD缺口沖擊強(qiáng)度 | 23℃1/2" | ASTM D-256 | 31 (5.5) | kg.cm/cm(Ft.1b/in) |
| IZOD缺口沖擊強(qiáng)度 | 1/8" 23℃ | ASTM D-256 | 45 (7.0) | kg.cm/cm(Ft.1b/in) | |
| 降伏點(diǎn)抗張強(qiáng)度 | 23℃ | ASTM D-638 | 410 | kg/cm2 | |
| 降伏點(diǎn)抗張強(qiáng)度 | 23℃ | ASTM D-256 | 5800 | psi | |
| 斷裂點(diǎn)抗張強(qiáng)度 | 1/8" | ASTM D-638 | 360 | kg/cm2 | |
| 斷裂點(diǎn)抗張強(qiáng)度 | 1/8" | ASTM D-638 | 5100 | psi | |
| 斷裂伸長(zhǎng)率 | 1/8" | ASTM D-638 | 40 | % | |
| 抗折強(qiáng)度 | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm2 | |
| 抗折強(qiáng)度 | 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi | |
| 抗折系數(shù) | 23℃ 2.8mm/min | ASTM D-790 | 21000 | kg/cm2 | |
| 抗折系數(shù) | 23℃ 2.8mm/min | ASTM D-790 | 300000 | psi | |
| 洛氏硬度 | 102 | ||||
| 熱性能 | 熱變形溫度 | 未退火 | ASTM D-648 | 86 (187) | ℃(F) |
| 維卡軟化點(diǎn) | ASTM D-1525 | 101 | ℃ | ||
| 阻燃等級(jí) | UL94 | HB | |||
ABS-3000D臺(tái)達(dá)化學(xué)
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。