PPA HTNFR52G20NH BK337,HTNFR52G20NH NC010,HTNFR52G30BL BK337,HTNFR52G30BL NC010,
| DuPont Performance Polymers Zytel? HTNFR52G20NH NC010 PA6T/66-GF20FR(40) | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyphthalamide (PPA); Polyphthalamide (PPA), 20% Glass Fiber Reinforced | ||
| Material Notes: |
20% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide
Information provided by DuPont Performance Polymers |
||
| Vendors: |
Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | DAM; ISO 294-4, 2577 | ||
| 0.0110 cm/cm | 0.0110 in/in | DAM; ISO 294-4, 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 50%RH; ISO 527-1/-2 | ||
| 135 MPa | 19600 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 2.20 % | 2.20 % | 50%RH; ISO 527-1/-2 | ||
| 2.40 % | 2.40 % | DAM; ISO 527-1/-2 | |||
| Tensile Modulus | 8.20 GPa | 1190 ksi | DAM; ISO 527-1/-2 | ||
| 8.60 GPa | 1250 ksi | 50%RH; ISO 527-1/-2 | |||
| Flexural Strength | 180 MPa | 26100 psi | 50%RH; ISO 178 | ||
| 215 MPa | 31200 psi | DAM; ISO 178 | |||
| Flexural Modulus | 7.80 GPa | 1130 ksi | DAM; ISO 178 | ||
| 8.20 GPa | 1190 ksi | 50%RH; ISO 178 | |||
Charpy Impact Unnotched 
|
3.00 J/cm2 @Temperature -30.0 °C |
14.3 ft-lb/in2 @Temperature -22.0 °F |
50%RH; ISO 179/1eU | ||
|
3.60 J/cm2 @Temperature 23.0 °C |
17.1 ft-lb/in2 @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |||
|
4.00 J/cm2 @Temperature 23.0 °C |
19.0 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eU | |||
|
4.00 J/cm2 @Temperature -30.0 °C |
19.0 ft-lb/in2 @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
|
Charpy Impact, Notched
|
0.600 J/cm2 @Temperature 23.0 °C |
2.86 ft-lb/in2 @Temperature 73.4 °F |
50%RH; ISO 179/1eA | ||
|
0.600 J/cm2 @Temperature 23.0 °C |
2.86 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eA | |||
|
0.600 J/cm2 @Temperature -30.0 °C |
2.86 ft-lb/in2 @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Dielectric Strength | 42.0 kV/mm | 1070 kV/in | DAM; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C | 13.9 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
|
21.0 μm/m-°C @Temperature 55.0 - 160 °C |
11.7 μin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | ||
|
27.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
15.0 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 68.0 μm/m-°C | 37.8 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
|
64.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
35.6 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | ||
|
100 μm/m-°C @Temperature 55.0 - 160 °C |
55.6 μin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |||
| Melting Point | 310 °C | 590 °F | first heat; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | DAM; ISO 75-1/-2 | ||
|
Flammability, UL94
|
V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
|
V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
DAM; IEC 60695-11-10 | |||
| Oxygen Index | 35.0 % | 35.0 % | DAM; ISO 4589-1/-2 | ||
|
Glow Wire Test
|
725 °C @Thickness 0.400 mm |
1340 °F @Thickness 0.0157 in |
Glow Wire Ignition Temperature; DAM; IEC 60695-2-1/2 | ||
|
960 °C @Thickness 0.400 mm |
1760 °F @Thickness 0.0157 in |
Glow Wire Flammability Index; DAM; IEC 60695-2-1/2 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 320 °C | >= 608 °F | |||
| <= 325 °C | <= 617 °F | ||||
| Mold Temperature | >= 85.0 °C | >= 185 °F | |||
| <= 130 °C | <= 266 °F | ||||
| Drying Temperature |
100 °C @Time 21600 - 28800 sec |
212 °F @Time 6.00 - 8.00 hour |
|||
| Moisture Content | 0.100 % | 0.100 % | |||
|
De |
|||||
| Additive | Lubricant | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Drying Recommended | yes | ||||
| Odor Class | 3.5 | VDA 270 | |||
| Part Marking Code | >PA6T/66-GF20FR(40)< | ISO 11469 | |||
| >PPA-GF20FR< | SAE J1344 | ||||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA6T/66-GF20FR(40) | ISO 1043 | |||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
Arlon 55191R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
Quadrant EPP Nylatron? GS Nylon, Extruded MoS2 Filled Type 66 (ASTM Product Data Sheet)
DuPont Performance Polymers Zytel? HTN92G35DH2 BK083 PA6T/66-GF35
PTS Trimid? N66-100L Lubed Nylon 6/6
Overview of materials for Liquid Crystal Polymer (LCP), 20% Glass Fiber Filled
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。
簡(jiǎn)繁切換