沙伯基礎(chǔ)創(chuàng)新塑料PEI ULTEM Resin 1110,1110F,
ULTEM ? Resin 1110
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 5 mm/min
1120
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
70
%
ASTM D 638
Tensile Modulus, 5 mm/min
37900
kgf/cm2
ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span
1680
kgf/cm2
ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span
37900
kgf/cm2
ASTM D 790
IMPACT
Value
Unit
Standard
Izod Impact, Reverse Notched, 3.2 mm
163
cm-kgf/cm
ASTM D 256
Gardner, 23°C
235
cm-kgf
ASTM D 3029
THERMAL
Value
Unit
Standard
HDT, 1.82 MPa, 6.4 mm, unannealed
198
°C
ASTM D 648
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.36
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 337°C/6.6 kgf
16
g/10 min
ASTM D 1238
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94V-0 Flame Class Rating (3)
0.75
mm
UL 94
UL Recognized, 94-5VA Rating (3)
3
mm
UL 94
Source GMD, last updated:2012/04/03
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
150
°C
Drying Time
4 - 6
hrs
Drying Time (Cumulative)
24
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
350 - 400
°C
Nozzle Temperature
345 - 400
°C
Front - Zone 3 Temperature
345 - 400
°C
Middle - Zone 2 Temperature
340 - 400
°C
Rear - Zone 1 Temperature
330 - 400
°C
Mold Temperature
135 - 165
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
40 - 60
%
Vent Depth
0.025 - 0.076
mm
Source GMD, last updated:2012/04/03
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。