SABIC沙伯基礎(chǔ)創(chuàng)新塑料PBT Valox 508R物性參數(shù)物性表
以下是SABIC沙伯基礎(chǔ)創(chuàng)新塑料PBT Valox 508R的中英文物性表
|
SABIC Innovative Plastics Valox? 508R PBT+PC
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Specific Gravity比重
|
1.50 g/cc
|
1.50 g/cc
|
ASTM D 792
|
|
Water Absorption吸水率
|
0.060 %
@Time 86400 sec |
0.060 %
@Time 24.0 hour |
ASTM D 570
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動(dòng)
|
0.0030 - 0.0050 cm/cm
@Thickness 1.50 - 3.20 mm |
0.0030 - 0.0050 in/in
@Thickness 0.0591 - 0.126 in |
SABIC Method
|
|
0.0050 - 0.0080 cm/cm
@Thickness 3.20 - 4.60 mm |
0.0050 - 0.0080 in/in
@Thickness 0.126 - 0.181 in |
SABIC Method
|
|
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向
|
0.0040 - 0.0060 cm/cm
@Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in
@Thickness 0.0591 - 0.126 in |
SABIC Method
|
|
0.0060 - 0.0090 cm/cm
@Thickness 3.20 - 4.60 mm |
SABIC Method
|
||
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Hardness, Rockwell R羅氏硬度R
|
119
|
119
|
ASTM D 785
|
|
Tensile Strength at Break斷裂拉伸強(qiáng)度
|
110 MPa
|
16000 psi
|
Type I, 5 mm/min; ASTM D 638
|
|
Flexural Strength彎曲強(qiáng)度
|
189 MPa
|
27400 psi
|
brk, 1.3 mm/min, 50 mm span; ASTM D 790
|
|
Flexural Modulus彎曲彈性模量
|
6.89 GPa
|
999 ksi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度
|
0.800 J/cm
@Temperature -30.0 °C |
1.50 ft-lb/in
@Temperature -22.0 °F |
ASTM D 256
|
|
0.960 J/cm
@Temperature 23.0 °C |
1.80 ft-lb/in
@Temperature 73.4 °F |
ASTM D 256
|
|
|
Izod Impact, Unnotched懸臂梁無(wú)缺口沖擊強(qiáng)度
|
6.40 J/cm
@Temperature 23.0 °C |
12.0 ft-lb/in
@Temperature 73.4 °F |
ASTM D 4812
|
|
Impact Test沖擊試驗(yàn)數(shù)據(jù)
|
6.00 J
@Temperature 23.0 °C |
4.43 ft-lb
@Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763
|
|
8.00 J
@Temperature 23.0 °C |
5.90 ft-lb
@Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763
|
|
|
Electrical Properties電性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Volume ResiSTivity體積電阻率
|
5.90e+16 ohm-cm
|
5.90e+16 ohm-cm
|
ASTM D 257
|
|
Dielectric Constantt介電常數(shù)
|
3.6
@Frequency 100 Hz |
3.6
@Frequency 100 Hz |
ASTM D 150
|
|
3.6
@Frequency 1.00e+6 Hz |
3.6
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Dielectric Strength介電強(qiáng)度
|
23.6 kV/mm
@Thickness 3.20 mm |
599 kV/in
@Thickness 0.126 in |
in air; ASTM D 149
|
|
29.1 kV/mm
@Thickness 1.60 mm |
739 kV/in
@Thickness 0.0630 in |
in oil; ASTM D 149
|
|
|
Dissipation Factor耗散因數(shù)
|
0.0014
@Frequency 100 Hz |
0.0014
@Frequency 100 Hz |
ASTM D 150
|
|
0.020
@Frequency 1.00e+6 Hz |
0.020
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Arc Resistance 耐電弧性
|
60 - 120 sec
|
60 - 120 sec
|
Tungsten, PLC code 6; ASTM D 495
|
|
Comparative Tracking Index相對(duì)漏電起痕指數(shù)
|
100 - 175 V
|
100 - 175 V
|
PLC code 4; UL 746A
|
|
Hot Wire Ignition, HWI熱線圈點(diǎn)燃測(cè)試
|
60 - 120 sec
|
60 - 120 sec
|
PLC code 1; UL 746A
|
|
High Amp Arc Ignition, HAI高電流電弧點(diǎn)燃測(cè)試
|
15 - 30 arcs
|
15 - 30 arcs
|
surface, PLC code 3; UL 746A
|
|
High Voltage Arc-Tracking Rate, HVTR高壓電弧跟蹤速度
|
25.4 - 80.0 mm/min
|
1.00 - 3.15 in/min
|
PLC code 2; UL 746A
|
|
Thermal Properties熱性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數(shù)
|
16.2 μm/m-°C
@Temperature 60.0 - 138 °C |
9.00 μin/in-°F
@Temperature 140 - 280 °F |
ASTM E 831
|
|
23.4 μm/m-°C
@Temperature -40.0 - 40.0 °C |
13.0 μin/in-°F
@Temperature -40.0 - 104 °F |
ASTM E 831
|
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
215 °C
@Thickness 6.40 mm |
419 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
176 °C
@Thickness 6.40 mm |
349 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
UL RTI, Electrical相對(duì)溫度指數(shù)
|
125 °C
|
257 °F
|
UL 746B
|
|
UL RTI, Mechanical with Impact機(jī)械沖擊熱指數(shù)
|
110 °C
|
230 °F
|
UL 746B
|
|
UL RTI, Mechanical without Impact無(wú)機(jī)械沖擊熱指數(shù)
|
125 °C
|
257 °F
|
UL 746B
|
|
Flammability, UL94阻燃等級(jí)
|
HB
@Thickness 1.47 mm |
HB
@Thickness 0.0579 in |
UL 94
|
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。