BASF Ultramid? B3EG3 PA6 GF15(尼龍6-聚酰胺)

特性：15%玻纖增強(qiáng)。供應(yīng)商：東莞市奧亞塑膠原料有限公司

Physical Properties物理性質(zhì)

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Density密度 

1.23 g/cc

0.0444 lb/in3

ISO 1183

Water Absorption吸水率 

7.7 - 8.3 %

7.7 - 8.3 %

Saturation; ISO 62

Moisture Absorption at Equilibrium吸濕平衡 

2.3 %

2.3 %

50% RH

2.3 - 2.9 %

2.3 - 2.9 %

23°C; 50% RH; ISO 62

7.7 %

7.7 %

Saturation

Viscosity Measurement粘度 

140

140

ISO 307

Linear Mold Shrinkage線性收縮率 

0.0045 cm/cm

0.0045 in/in

restricted

Melt Flow熔體流動(dòng)速率 

92.25 g/10 min
@Load 5.00 kg,
Temperature 275 °C

92.25 g/10 min
@Load 11.0 lb,
Temperature 527 °F

ISO 1133

Mechanical Properties力學(xué)性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Tensile Strength at Break斷裂拉伸強(qiáng)度 

103 MPa

14900 psi

ASTM D638

Tensile Strength, Yield屈服拉伸強(qiáng)度 

130 MPa

18900 psi

50 mm/min; ISO 527-1/-2

Elongation at Break斷裂伸長(zhǎng)率 

3.5 %

3.5 %

ASTM D638

Elongation at Yield屈服伸長(zhǎng)率 

3.5 %

3.5 %

50 mm/min; ISO 527-1/-2

Modulus of Elasticity彈性模量 

5.80 GPa

841 ksi

ISO 527-1/-2

Flexural Strength彎曲強(qiáng)度 

180 MPa

26100 psi

at max force; ISO 178

Flexural Modulus彎曲彈性模量 

5.20 GPa

754 ksi

ISO 178

Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 (ISO) 

6.00 kJ/m2
@Temperature 23.0 °C

2.86 ft-lb/in2
@Temperature 73.4 °F

ISO 180/A

Charpy Impact Unnotched夏比缺口試樣沖擊 

4.50 J/cm2
@Temperature -30.0 °C

21.4 ft-lb/in2
@Temperature -22.0 °F

ISO 179/1eU

4.80 J/cm2
@Temperature -40.0 °C

22.8 ft-lb/in2
@Temperature -40.0 °F

ASTM D256

5.00 J/cm2
@Temperature 23.0 °C

23.8 ft-lb/in2
@Temperature 73.4 °F

ISO 179/1eU

Charpy ImPAct, Notched夏比缺口沖擊 

0.700 J/cm2
@Temperature -30.0 °C

3.33 ft-lb/in2
@Temperature -22.0 °F

ISO 179/1eA

0.800 J/cm2
@Temperature 23.0 °C

3.81 ft-lb/in2
@Temperature 73.4 °F

ISO 179/1eA

Electrical Properties電性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Volume ResiSTivity體積電阻率 

1.00e+13 ohm-cm

1.00e+13 ohm-cm

IEC 60093

Dielectric Constant介電常數(shù) 

3.8
@Frequency 1.00 Hz

3.8
@Frequency 1.00 Hz

IEC 60250

Dissipation Factor耗散因數(shù) 

0.025
@Frequency 1.00e+6 Hz

0.025
@Frequency 1.00e+6 Hz

IEC 60250

Comparative Tracking Index跟蹤指數(shù) 

550 V

550 V

Test solution A; IEC 60112

Thermal Properties熱性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

CTE, linear 線性熱膨脹系數(shù)

0.200 μm/m-°C

0.111 μin/in-°F

ASTM E831

CTE, linear, Parallel to Flow線性熱膨脹系數(shù) 

0.300 - 0.350 μm/m-°C
@Temperature 23.0 - 80.0 °C

0.167 - 0.194 μin/in-°F
@Temperature 73.4 - 176 °F

DIN 11359-1/-2

CTE, linear, Transverse to Flow線性熱膨脹系數(shù)/橫向 

0.700 - 0.800 μm/m-°C
@Temperature 23.0 - 80.0 °C

0.389 - 0.444 μin/in-°F
@Temperature 73.4 - 176 °F

DIN 11359-1/-2

Specific Heat Capacity比熱容 

1.60 J/g-°C

0.382 BTU/lb-°F

Thermal Conductivity導(dǎo)熱系數(shù) 

0.340 W/m-K

2.36 BTU-in/hr-ft2-°F

DIN 52612

Melting Point熔點(diǎn) 

220 °C

428 °F

DIN 53765

Maximum Service Temperature, Air高使用溫度 

200 °C

392 °F

Deflection Temperature at熱變形溫度0.46 MPa (66 psi) 

215 °C

419 °F

ISO 75-1/-2

Deflection Temperature at熱變形溫度1.8 MPa (264 psi) 

190 °C

374 °F

ISO 75-1/-2

UL RTI, Electrical相對(duì)溫度指數(shù) 

120 °C
@Thickness 1.50 mm

248 °F
@Thickness 0.0591 in

746B

UL RTI, Mechanical with Impact機(jī)械沖擊熱指數(shù) 

95.0 °C
@Thickness 1.50 mm

203 °F
@Thickness 0.0591 in

746B

UL RTI, Mechanical without Impact 無(wú)機(jī)械沖擊熱指數(shù)

130 °C
@Thickness 1.50 mm

266 °F
@Thickness 0.0591 in

746B

Flammability, UL94阻燃等級(jí) 

HB
@Thickness 1.60 mm

HB
@Thickness 0.0630 in

Processing Properties加工性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Melt Temperature熔體溫度 

270 - 290 °C

518 - 554 °F

Injection-molding/Extrusion

Mold Temperature模具溫度 

80.0 - 90.0 °C

176 - 194 °F

Injection-molding

Dry Time干燥時(shí)間 

2 - 4 hour

2 - 4 hour